Ag–TiCN coatings were deposited by dc reactive magnetron sputtering and their structural and morphological properties were evaluated. Compositional analysis showed the existence of Ag–TiCN coatings with different Ag/Ti atomic ratios (ranging from 0 to 1.49). The structural and morphological properties are well correlated with the evolution of Ag/Ti atomic ratio. For the samples with low Ag/Ti atomic ratio (below 0.20) the coatings crystallize in a B1-NaCl crystal structure typical of TiC0.3N0.7. The increase in Ag/Ti atomic ratio promoted the formation of Ag crystalline phases as well as amorphous CNx phases detected in both x-ray photoelectron spectroscopy and Raman spectroscopy analysis. Simultaneously to the formation of Ag crystalline phases and amorphous carbon-based phases, a decrease in TiC0.3N0.7 grain size was observed as well as the densification of coatings.

Pertenece a

RepositóriUM Universidade do Minho  

Autor(es)

Manninen, N. K. -  Galindo, R. Escobar -  Benito, N. -  Figueiredo, N. M. -  Cavaleiro, A. -  Palacio, C. -  Carvalho, S. - 

Id.: 57984311

Idioma: eng  - 

Versión: 1.0

Estado: Final

Tipo de recurso: article  - 

Tipo de Interactividad: Expositivo

Nivel de Interactividad: muy bajo

Audiencia: Estudiante  -  Profesor  -  Autor  - 

Estructura: Atomic

Coste: no

Copyright: sí

: open access

Requerimientos técnicos:  Browser: Any - 

Fecha de contribución: 04-ago-2015

Contacto:

Localización:

Aviso de cookies: Usamos cookies propias y de terceros para mejorar nuestros servicios, para análisis estadístico y para mostrarle publicidad. Si continua navegando consideramos que acepta su uso en los términos establecidos en la Política de cookies.