It has been demonstrated that a Cs 2 O-stabilized leucite porcelain was susceptible to a stress-induced phase transformation, but toughening was not observed. 1 It was hypothesized that if Cs 2 O-stabilized leucite core particles were added to a cesium-free matrix porcelain, selected or designed to enhance the toughening mechanism, toughening would occur. A commercial porcelain (VP) and a synthesized leucite-based porcelain (NP) were the matrix materials. Core particles of Cs 2 O (0.0–2.0 mol%) containing synthetic leucite were mixed with the two cesium-free matrix porcelains and vacuum fired into specimens for testing. The toughness of both types of matrix-based materials was dependent upon cesium content of the added core particles with a maximum toughness reached for those containing 0.75 mol% Cs 2 O. The toughness of the 0.75 mol% specimens (1.42 MNm −3/2 for VP based and 2.15 MNm −3/2 for NP based) was statistically ( p < .02) higher than either of the matrix materials alone or the matrix materials containing added core particles of synthetic cesium-free leucite. However, the toughest materials (0.75 mol% Cs 2 O) were not the strongest materials, most likely because of large internal flaws. The results suggested that transformation toughening was possible. © 2004 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 69B: 195–204, 2004

Pertenece a

Deep Blue at the University of Michigan  

Autor(es)

Rasmussen, Stephen T. -  McLaren, Charles I. -  O'Brien, William Joseph - 

Id.: 51914401

Idioma: inglés (Estados Unidos)  - 

Versión: 1.0

Estado: Final

Tipo:  278125 bytes -  3118 bytes -  application/pdf -  text/plain - 

Palabras claveChemistry - 

Tipo de Interactividad: Expositivo

Nivel de Interactividad: muy bajo

Audiencia: Estudiante  -  Profesor  -  Autor  - 

Estructura: Atomic

Coste: no

Copyright: sí

: IndexNoFollow

Formatos:  278125 bytes -  3118 bytes -  application/pdf -  text/plain - 

Requerimientos técnicos:  Browser: Any - 

Fecha de contribución: 01-sep-2010

Contacto:

Localización:
* Rasmussen, Stephen T.; McLaren, Charles I.; O'Brien, William J. (2004)."The effect of cesium-containing leucite additions on the thermal and mechanical properties of two leucite-based porcelains." Journal of Biomedical Materials Research 69B(2): 195-204.
* 0021-9304
* 1097-4636
* Journal of Biomedical Materials Research

Aviso de cookies: Usamos cookies propias y de terceros para mejorar nuestros servicios, para análisis estadístico y para mostrarle publicidad. Si continua navegando consideramos que acepta su uso en los términos establecidos en la Política de cookies.