  1. Failure analysis of prestressed anchor bars

    Elices, M.; Valiente, Andrés; Caballero, L.; Iordachescu, M.; Fullea, J.; Sánchez-Montero, J.; López, Víctor
    Three broken steel bars from a sewed crack in a dam are reported. The inspection of the fracture surfaces of the prestressed bars suggests that fractures were triggered by small cracks and by the inherent brittleness of the bars, as fracture toughness was about 40MPam 1/2. The analysis of the failures shows that the usual design requirements for prestressing bars fail to warn against brittle failures if some damage exists. Some recommendations, based on the concept of damage tolerance, are suggested to avoid similar unfortunate incidents. © 2012 Elsevier Ltd.
    - 13-ene-2018

  2. Failure analysis of prestressed anchor bars

    Elices, M.; Valiente, Andrés; Caballero, L.; Iordachescu, M.; Fullea, J.; Sánchez-Montero, J.; López, Víctor
    Three broken steel bars from a sewed crack in a dam are reported. The inspection of the fracture surfaces of the prestressed bars suggests that fractures were triggered by small cracks and by the inherent brittleness of the bars, as fracture toughness was about 40MPam 1/2. The analysis of the failures shows that the usual design requirements for prestressing bars fail to warn against brittle failures if some damage exists. Some recommendations, based on the concept of damage tolerance, are suggested to avoid similar unfortunate incidents. © 2012 Elsevier Ltd.
    - 17-ene-2018

  3. 6th Meeting of the Spanish Neutron Scattering Association (SETN2012): Preface

    Hernández-Velasco, Jorge; Cabrillo García, Carlos; Castellote, M.; Ruiz-Hervías, Jesús
    1 pag.; VI Reunión de la Sociedad Española de Técnicas Neutrónicas (SETN), Segovia, 24-27 de junio de 2012
    - 13-ene-2018

  4. La comisión de mujeres y ciencia del CSIC: Diez años promoviendo la igualdad de oportunidades en el organismo

    López-Sancho, María Pilar; Alvarez-Marrón, Joaquina; Pablo, Flora de; Masegosa, Josefa; Mayoral Gastón, María del Carmen; Molina, Elena; Pérez Sedeño, Eulalia; Puertas, Francisca; Sandalio, Luisa M.
    Este es un artículo de acceso abierto distribuido bajo los términos de la licencia Creative Commons Attribution-Non Commercial (by-nc) Spain 3.0.
    - 10-jul-2018

Aviso de cookies: Usamos cookies propias y de terceros para mejorar nuestros servicios, para análisis estadístico y para mostrarle publicidad. Si continua navegando consideramos que acepta su uso en los términos establecidos en la Política de cookies.